FeCrAl Electric Heating 0Cr25Al5 Resistance Wire
Contact me for free samples and coupons.
WhatsApp:0086 18588475571
WeChat: 0086 18588475571
skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Details
| Delivery Time | 7-20 Days | Material | Ferrous Chromium Aluminum |
|---|---|---|---|
| Resistivity | 1.42+/-0.05 | Tensile Strength | 630-780MPA |
| Elongtation | ≥12% | Application | Heating, Resistivity |
| Condition | Hard / Soft | Sureface | Bright, Oxided, Acide |
| Maximum Temperature | 1250℃ | Melting Point | 1500℃ |
| Name | 0Cr25Al5 Resistance Wire | ||
| Highlight | 0Cr25Al5 Resistance Wire,FeCrAl Electric Heating Resistance Wire,Oxide Surface FeCrAl Alloy |
||
Product Description
High quality hot sale FeCrAl electric heating 0Cr25Al5 resistance wire
- FeCrAl Series
0Cr25Al5 resistance wire is a kind of iron, chromium and aluminum with high resistivity, low resistivity, high working temperature, good oxidation resistance at high temperature, and the highest applicable temperature is up to 1250 degrees. The alloy is mainly used to make ceramic electric cookers, industrial furnaces, and various electric heating elements.
0Cr25Al5 resistance wire intended for prolonged operation at high temperature. Iron Chromium Aluminum alloy wires are used chiefly for heating elements in the electrical industry and wide range of high-temperature oxidation environments, such as industrial electric furnace, heating furnace, nuclear reactor, petroleum refinery and automotive exhaust system, household electrical appliance, electrical oven, electrical heater, infrared settings and far infrared ray device.
0Cr25Al5 resistance wire's ability to withstand oxidation, the wires can be employed under high-temperature conditions, while their good ductility enables them to be processed into wire and strip by hot and cold working.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
|