Heating Alloy 0Cr21Al6 Electric Resistance Wire Used For Home Appliances
Contact me for free samples and coupons.
WhatsApp:0086 18588475571
WeChat: 0086 18588475571
skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xDelivery Time | 7-20 Days | Material | Ferrous Chromium Aluminum |
---|---|---|---|
Resistivity | 1.42+/-0.05 | Tensile Strength | 630-780MPA |
Elongtation | ≥12% | Application | Heating, Resistivity |
Condition | Hard / Soft | Sureface | Bright, Oxided, Acide |
Maximum Temperature | 1250℃ | Melting Point | 1500℃ |
Name | Resistance Heating Wire |
- FeCrAl Series
0Cr21Al6 resistance wire is widely used in industrial and electrical fields, mainly in heating elements, resistors, thermocouples, and more.
0Cr21Al6 resistance wire is a commonly used electric heating alloy material with various applications in household appliances.
- Ovens and Oven Light Bulbs
0Cr21Al6 resistance wire is widely used as heating elements in ovens and oven light bulbs. They generate high temperatures inside the oven for baking food and provide illumination.
- Dryers
In dryers, 0Cr21Al6 resistance wire serves as heating elements to help heat and dry clothes, bedding, etc.
- Electric Kettles and Coffee Machines
Heating elements inside electric kettles and coffee machines often utilize 0Cr21Al6 resistance wire to quickly heat water or coffee, providing users with hot beverages.
- Water Heaters
In household water heaters, 0Cr21Al6 resistance wire is used as heating elements to help heat water for bathing, washing, etc.
- Electric Blankets
Electric blankets are bedding items used to provide extra warmth, and the heating elements inside them typically employ 0Cr21Al6 resistance wire to maintain a warm and comfortable bed.
- Ferrous Chromium Aluminum alloy performance tables
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Magnetic |
- The Form we could offer