Oxidation Resistance Fecral Alloy 0cr21al6 Heating Resistance Wire For Resistors
Contact me for free samples and coupons.
WhatsApp:0086 18588475571
WeChat: 0086 18588475571
skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xDelivery Time | 7-20 Days | Material | Ferrous Chromium Aluminum |
---|---|---|---|
Resistivity | 1.42+/-0.05 | Tensile Strength | 630-780MPA |
Elongtation | ≥12% | Application | Heating, Resistivity |
Condition | Hard / Soft | Sureface | Bright, Oxided, Acide |
Maximum Temperature | 1250℃ | Melting Point | 1500℃ |
Name | Resistance Heating Wire |
- FeCrAl Series
0Cr21Al6 resistance wire is widely used in industrial and electrical fields, mainly in heating elements, resistors, thermocouples, and more.
0Cr21Al6 resistance wire is commonly used in resistors. Resistors are electronic components used to limit current or adjust voltage in circuits.
- High Temperature Stability
Due to its excellent high-temperature stability and oxidation resistance, 0Cr21Al6 resistance wire can operate stably in high-temperature environments.
- Low Temperature Coefficient
The temperature coefficient of the 0Cr21Al6 resistance wire is low, allowing it to maintain a relatively stable resistance value over a wide temperature range.
- Injection Molding Machine Heaters
Heating elements in injection molding machine heaters often utilize 0Cr21Al6 resistance wire to heat and maintain the flow state of plastics during the injection molding process.
- High Resistance Value
This resistance wire can achieve high resistance values, making it suitable for circuit designs that require high resistance.
- Long Lifespan
0Cr21Al6 resistance wire has good wear resistance and corrosion resistance, thus offering a longer lifespan.
- Ferrous Chromium Aluminum alloy performance tables
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Magnetic |
- The Form we could offer